Fracture performance of a PCM-Rich concrete pavement under thermal stresses

Naser P. Sharifi, Sina Askarinejad, Kamyar C. Mahboub

Research output: Contribution to journalArticlepeer-review

6 Scopus citations

Abstract

Curling stresses in rigid pavements are the result of temperature gradient through the thickness of the concrete slab. These stresses have a periodic nature, and the induced cyclic flexural curling stresses lead to the cracking of the concrete slab. In a previous research by the authors, a phase change material (PCM)-rich concrete overlay was proposed as an effective method to control this failure mechanism. A PCM-rich concrete overlay is a concrete surface layer that contains a relatively high percentage of PCM. In the previous study, a phenomenological approach was employed, and it was demonstrated that the incorporation of PCM improves the curling fatigue performance of the concrete slab. Using fracture mechanics, this paper builds upon the findings of the previous study, and it serves as a mechanistic verification of the conclusions of the previous work. A modified Paris’ Law was adopted to calculate the cumulative fatigue-fracture damage of the concrete slab due to cyclic thermally-induced curling stresses. The findings of this research demonstrated that the PCM-modified concrete slab undergoes a curling-induced fracture process that is less severe than the slab without the PCM. The impact of this reduction was quantified in terms of an improved fatigue-fracture performance of the pavement.

Original languageEnglish
Pages (from-to)221-230
Number of pages10
JournalInternational Journal of Pavement Engineering
Volume23
Issue number2
DOIs
StatePublished - 2022

Bibliographical note

Publisher Copyright:
© 2020 Informa UK Limited, trading as Taylor & Francis Group.

Keywords

  • Paris’ law
  • Phase change materials
  • concrete fracture
  • concrete pavements
  • curling stresses

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Mechanics of Materials

Fingerprint

Dive into the research topics of 'Fracture performance of a PCM-Rich concrete pavement under thermal stresses'. Together they form a unique fingerprint.

Cite this