Wettability investigating on the wet etching textured multicrystalline silicon wafer

In order to investigate the wettability properties of multicrystalline silicon (mc-Si), the different surface structures were fabricated on the as-cut p-type multi-wire slurry sawn mc-Si wafers, such as as-cut, polished and etched in various acid solutions. The contact angles and the XRD spectra of these samples were measured. It was noted that both the surface structures and the use of surfactant, such as Tween 80, made a stronger effect on wettability of the Si wafer. Due to the lipophilic groups of Tween 80 combined with the Si atoms while the hydrophilic groups of it were outward, a lipophilic surface of Si changed into a hydrophilic one and the rougher the surface, the stronger the hydrophily. Thus, it is feasible to add an appropriate surfactant into the etching solution during black-Si wafer fabrication for solar cells. In addition, different crystal plains of Si had different dangling bond density, so that their surface energies were different. A surface with higher surface energy could attract more water atoms and its wettability was better. However, the effect of crystal plain on the surface wettability was much weaker than surface morphology.